How to make carbon steel pipe?

Release time:
2024-09-10
The raw material for carbon steel pipes is round tube billet. The round tube billet must be cut by a cutting machine into a billet with a length of about 1 meter and sent to the furnace for heating via a conveyor belt. The billet is fed into the furnace and heated to a temperature of approximately 1,200 degrees Celsius. The fuel is hydrogen or acetylene. Temperature control in the furnace is a key issue. After the round tube comes out of the furnace, it must be pierced through a pressure punching machine. Generally, the more common piercing machine is the tapered roller piercing machine. This type of piercing machine has high production efficiency, good product quality, large perforation diameter expansion, and can penetrate a variety of steel types. After perforation, the round tube blank is successively cross-rolled, continuous rolled or extruded by three rollers. After extrusion, the pipe should be removed and calibrated. The sizing machine rotates a tapered drill bit at high speed into the steel blank to drill holes to form a steel pipe. The inner diameter of the steel pipe is determined by the outer diameter length of the drill bit of the sizing machine. After the steel pipe is sized, it enters the cooling tower and is cooled by spraying water. After the steel pipe is cooled, it will be straightened. After straightening, the steel pipe is sent to the metal flaw detector (or hydraulic test) by the conveyor belt for internal flaw detection. If there are cracks, bubbles and other problems inside the steel pipe, they will be detected. After quality inspection, steel pipes must undergo strict manual selection. After the quality inspection of the steel pipe, spray the serial number, specification, production batch number, etc. with paint. And it is hoisted into the warehouse by a crane.
Latest News
How to make carbon steel pipe?
2024-09-10
Stainless steel rod production process
2024-08-22
Types and specifications of angle steel
2024-07-19
Cold rolled steel processing methods
2024-06-28
2024-05-02